CHEMICAL COMPOSITION Cr2O3 ≥46.0% SiO2 ≤1.0% FeO ≤26.5% CaO ≤0.3% MgO ≤10% AL2O3 ≤15.5% P ≤0.003% S ≤0.003% Cr/Fe 1.55:1 TYPICAL PHYSICAL PROPERTIES Hardness: Mohs:5.5-6 Melting Point: Sublimes at 2180 ℃ Sintering point: >1800℃ The sintered 1600℃ Specific Gravity: 4.0-4.8 g/cm3 Bulk density(LPD): 2.5-3 g/cm3 Color: Black PH 7-9 Percentage of free acid present in the

Chromite sand is a naturally occurring spinel consisting primarily of the oxides of chrome and iron. It is a by-product of ferro-chrome production and is mainly used in foundry applications and in glass production.   Technical Data Sheet of Foundry Chromite sand:  CHEMICAL COMPOSITION Cr2O3 ≥46.0% SiO2 ≤1.0% FeO ≤26.5% CaO ≤0.3% MgO ≤10% AL2O3 ≤15.5%

Chromite sand is a naturally occurring spinel consisting primarily of the oxides of chrome and iron. It is a by-product of ferro-chrome production and is mainly used in foundry applications and in glass production. Technical Data Sheet of Foundry Chromite sand:  CHEMICAL COMPOSITION Cr2O3 ≥46.0% SiO2 ≤1.0% FeO ≤26.5% CaO ≤0.3% MgO ≤10% AL2O3 ≤15.5% P

Technical Data Sheet of Foundry Chromite sand:  CHEMICAL COMPOSITION Cr2O3 ≥46.0% SiO2 ≤1.0% FeO ≤26.5% CaO ≤0.3% MgO ≤10% AL2O3 ≤15.5% P ≤0.003% S ≤0.003% Cr/Fe 1.55:1 TYPICAL PHYSICAL PROPERTIES Hardness: Mohs:5.5-6 Melting Point: Sublimes at 2180 ℃ Sintering point: >1800℃ The sintered 1600℃ Specific Gravity: 4.0-4.8 g/cm3 Bulk density(LPD): 2.5-3 g/cm3 Color: Black PH 7-9

Technical Data Sheet of Foundry Chromite sand:  CHEMICAL COMPOSITION Cr2O3 ≥46.0% SiO2 ≤1.0% FeO ≤26.5% CaO ≤0.3% MgO ≤10% AL2O3 ≤15.5% P ≤0.003% S ≤0.003% Cr/Fe 1.55:1 TYPICAL PHYSICAL PROPERTIES Hardness: Mohs:5.5-6 Melting Point: Sublimes at 2180 ℃ Sintering point: >1800℃ The sintered 1600℃ Specific Gravity: 4.0-4.8 g/cm3 Bulk density(LPD): 2.5-3 g/cm3 Color: Black PH 7-9

Chrome Sand is often used in the moulds for automotive castings, like engine blocks and camshafts, but it is preferred for many other foundry uses because of its resilient characteristics. Chrome Sand is also used as a primary material in the production of green glass, in well fillers, and to augment the refractory fire brick